Tritan™ LX150HF
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2ng6gV_Tritan-LX150HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Tritan™ LX150HF is a high flow grade of an amorphous copolyester with excellent appearance and clarity. Eastman Tritan™ LX150HF has viscosity reductions of 40-50% relative to standard grades of Eastman Tritan™. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. Tritan™ LX150HF was developed for the cosmetic, fragrance, and personal care markets. Tritan™ LX150HF can easily be converted into articles for application in consumer and personal care markets by injection molding, extrusion blow molding, and injection blow molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1580 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 43.0 | MPa | |
| Break, 23°C | 52.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 7.0 | % | |
| Break, 23°C | 210 | % | |
| Flexural Modulus (23°C) | 1580 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 64.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 110 | J/m | |
| 23°C | 860 | J/m | |
| Unnotched Izod Impact | ASTM D256 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 57.0 | J | |
| 23°C, Energy at Peak Load | 53.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 94.0 | °C | |
| 1.8 MPa, Unannealed | 81.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total) | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 38.0 to 66.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WanBlend® WHT-HF8485K2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| Kingfa NH-627 | Kingfa | ABS | Kingfa |
| INLUBE PA6GF30TF13SI2 | Infinity LTL Engineered Compounds | Nylon 6 | INLUBE |
| Plenco 08235 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |
| Sylvin 8200-75 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |