Menzolit® SMC 0430
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2mup2h_Menzolit-SMC-0430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 0430 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is highly recomended to mould in chrome plated moulds. The product contains no halogens nor any heavy metals. Menzolit® SMC 0430 is a low emission Class-A SMC for on-line painted exterior body applications on passenger cars. These compounds mould to parts with excellent surface quality for on-line painted body panels at high paint bake temperatures (190- 200 °C). The parts have to be primed with a conductive primer before e-coating. In addition to the excellent surface quality that these parts provide they also are designed with a special matrix that allows drastically reduction of emissions, smell and fogging. Moulded parts comply with all regulations of the automotive industry including low C-emissions.Surface defects like waviness, fibre patterns and orange peel are not existent with this product. To achieve the highest surface quality, we recommend that tool surfaces are mirror polished. The excellent temperature resistance of Menzolit® SMC 0430 allows online painting at high bake temperatures (190- 200 °C). The parts show very good adhesion to paint or In Mould Coating (IMC). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.82 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | -0.050 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 10000 | MPa | ISO 14125 |
| Flexural Stress | 165 | MPa | ISO 14125 |
| Poisson's Ratio | 0.30 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fiber Content | 28 | % | ISO 1172 |
| Material Designation | >UP-(GF+KD)70)< | EN 14598-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 66 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (4.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 145 to 155 | °C | |
| Injection Pressure | 6.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PVC Film 165 NT | Teknor Apex Company | PVC, Flexible | PVC Film |
| Ultramid® A3U40G5 | BASF Corporation | Nylon 66 | Ultramid® |
| CoolPoly® D5108 | Celanese Corporation | PPS | CoolPoly® |
| Latamid SP2 H2 G/45 | LATI S.p.A. | Nylon 612 | Latamid |
| InnoClear™ OC-5070 | Innovative Polymers, Inc. | TSU | InnoClear™ |