MACOMASS PP MM-PP HI 21 (10% Talc)
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | MACOMASS Verkaufs AG |
| Trademark: | MACOMASS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2mQYmP_MACOMASS-PP-MM-PP-HI-21-10-Talc-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MACOMASS PP MM-PP HI 21 (10% Talc) is a Polypropylene Homopolymer (PP Homopolymer) material filled with 10% talc. It is available in Europe. Primary attribute of MACOMASS PP MM-PP HI 21 (10% Talc): Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 to 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 to 21 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 83.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 10 | % | ISO 527-2 |
| Flexural Modulus | > 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | > 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | > 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 107 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-MFC-G0 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Ultrason® E 7020 P | BASF Corporation | PESU | Ultrason® E |
| Bynel® 3126 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| HiFill® POM CO GF5 CC | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| LCA® 100P Type | UniPlas, Inc. | Acetal (POM) Homopolymer | LCA® |