Trademark PE mLLD1918C
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Trademark Plastics Corporation |
| Trademark: | Trademark PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2mEPo0_Trademark-PE-mLLD1918C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trademark PE mLLD1918C is a Metallocene Linear Low Density Polyethylene product. It can be processed by coextrusion and is available in North America. Applications of Trademark PE mLLD1918C include film, food contact applications, packaging and sealing applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Force (25 µm) | 77.0 | N | ASTM D3763 |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 172 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 190 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 10.7 | MPa | |
| TD : Yield, 25 µm, Blown Film | 9.51 | MPa | |
| MD : Break, 25 µm, Blown Film | 58.5 | MPa | |
| TD : Break, 25 µm, Blown Film | 51.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 450 | % | |
| TD : Break, 25 µm, Blown Film | 600 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 800 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 230 | g | |
| TD : 25 µm, Blown Film | 500 | g | |
| Seal Initiation Temperature (25 µm, Blown Film) | 95.6 | °C | ASTM D3763 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 130 | ASTM D2457 | |
| Haze 2(25.4 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 to 204 | °C |
| Note Message | |
|---|---|
| 1 . | Base polymer only |
| 2 . | Base polymer only |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman PC SP910 | Shuman Plastics, Inc. | PC | Shuman PC |
| Boda BDT-KR3752 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Fainplast PVC KLT 87/UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Ixef® 1524 | Solvay Specialty Polymers | PARA | Ixef® |
| LNP™ LUBRICOMP™ QCL349 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |