VICTREX® PEEK 90GL30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2lbCh3_VICTREX-PEEK-90GL30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food contact compliant, colour natural/beige. Complex geometries with thinner cross sections or longer flow lengths where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.52 | g/cm³ | ISO 1183 |
| Spiral Flow 2 | Internal method | ||
| -- 3 | 18.5 | cm | Internal method |
| -- 4 | 22.0 | cm | Internal method |
| Molding Shrinkage 5 | ISO 294-4 | ||
| Vertical flow direction : 180°C | 0.90 | % | ISO 294-4 |
| Flow direction : 180°C | 0.30 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.040 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 87 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 190 | MPa | ISO 527-2 |
| Fracture, 125°C | 130 | MPa | ISO 527-2 |
| Fracture, 175°C | 80.0 | MPa | ISO 527-2 |
| Fracture, 225°C | 60.0 | MPa | ISO 527-2 |
| Fracture, 275°C | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.3 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 290 | MPa | ISO 178 |
| 125°C | 190 | MPa | ISO 178 |
| 175°C | 80.0 | MPa | ISO 178 |
| 275°C | 50.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 250 | MPa | ISO 604 |
| 120°C | 160 | MPa | ISO 604 |
| 250°C | 55.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 8.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 343 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | ISO 11357-2 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : > 143°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : < 143°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1700 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.30 | W/m/K | ISO 22007-4 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C, 1 MHz) | 3.30 | IEC 60250 | |
| Dissipation Factor (23°C, 1 MHz) | 4.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 220 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 355 | °C | |
| Middle Temperature | 360 | °C | |
| Front Temperature | 365 | °C | |
| Nozzle Temperature | 370 | °C | |
| Mold Temperature | 170 - 200 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | Crystalline |
| 2 . | 1 mm |
| 3 . | Mold temperature: 180°C, melt temperature: 370°C |
| 4 . | Mold temperature: 200°C, melt temperature: 400°C |
| 5 . | 370°C nozzle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA I LDPE B22/1 | ROMPETROL PETROCHEMICALS S.R.L. | LDPE | MIDILENA I |
| Niuk 23NT70 | Shanghai Niuk New Plastic Technology Co., Ltd. | PC+ABS | Niuk |
| DOMAMID® 6G15FC | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Lucofin® 1400SL | Lucobit AG | EBA | Lucofin® |
| POCAN® BFN 4211 000000 000000 | LANXESS Asia/Pacific | PBT | POCAN® |