Generic Nylon 6 - Carbon Fiber
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2kWY35_Generic-Nylon-6---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.17 - 1.43 | g/cm³ | ASTM D792 |
| 23°C | 1.16 - 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.055 - 0.30 | % | ASTM D955 |
| 23°C | 0.18 - 0.81 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.40 - 1.3 | % | ASTM D570 |
| 23°C, 24 hr | 0.99 - 1.3 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 - 2.4 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 88 - 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 6890 - 26500 | MPa | ASTM D638 |
| 23°C | 6950 - 20000 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 90.0 - 230 | MPa | ISO 527-2 |
| Fracture, 23°C | 90.0 - 233 | MPa | ASTM D638 |
| Fracture, 23°C | 129 - 201 | MPa | ISO 527-2 |
| 23°C | 117 - 234 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 3.5 | % | ASTM D638 |
| Yield, 23°C | 2.5 - 3.0 | % | ISO 527-2 |
| Fracture, 23°C | 1.5 - 3.1 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 3.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6830 - 20900 | MPa | ASTM D790 |
| 23°C | 5500 - 19000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 213 - 331 | MPa | ASTM D790 |
| 23°C | 191 - 315 | MPa | ISO 178 |
| Coefficient of Friction | 0.090 - 0.24 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 - 81 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 43 - 110 | J/m | ASTM D256 |
| 23°C | 0.80 - 15 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 320 - 810 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 215 - 216 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 200 - 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 204 - 218 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 190 - 211 | °C | ISO 75-2/A |
| Continuous Use Temperature | 90.0 - 91.0 | °C | ASTM D794 |
| Vicat Softening Temperature | 200 - 220 | °C | ISO 306 |
| CLTE - Flow | |||
| -- | 1.8E-5 - 2.0E-5 | cm/cm/°C | ASTM D696 |
| -- | 2.0E-5 - 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 55 - 2.5E+7 | ohms | ASTM D257 |
| -- | 10 - 2.5E+13 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 5.5 - 2.5E+13 | ohms·cm | ASTM D257 |
| 23°C | 5.0 - 2.5E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 105 | °C | |
| Drying Time | 2.0 - 13 | hr | |
| Suggested Max Moisture | 0.10 - 0.20 | % | |
| Rear Temperature | 254 - 282 | °C | |
| Middle Temperature | 259 - 282 | °C | |
| Front Temperature | 259 - 290 | °C | |
| Nozzle Temperature | 275 - 277 | °C | |
| Processing (Melt) Temp | 250 - 283 | °C | |
| Mold Temperature | 69.9 - 100 | °C | |
| Injection Pressure | 86.0 - 95.8 | MPa | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Screw Speed | 45 - 56 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9B22230 H | 4Plas | Nylon 6 | 4MID® |
| Adell Polyamide BJ-13 Glass Reinforced Mineral Filled | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Diamond ABS 3501 GF-10 | Network Polymers, Inc. | ABS | Diamond ABS |
| Karina WHITE PVC COMPOUND 750-10/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PEARLSTICK® 45-50/03 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |