CALIBRE™ 201-15
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2kW72u_CALIBRE-201-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 200-15 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistance, heat distortion resistance and optical clarity. The CALIBRE 200-15 series products are available in 4 additive packages: CALIBRE 200: No mold release or UV Stabilizer. CALIBRE 201: Mold release. CALIBRE 202: UV stabilizer. CALIBRE 203: Mold release and UV stabilizer. (Note that CALIBRE 202 and 203 grades are not available in Europe and do not comply with EU food contact regulations). Govt. and Industry Standards
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792, ISO 1183/A |
| -- | 1200 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Melt volume-flow rate (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 72 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 2340 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50, ISO 527-2 4 |
| Tensile Strength | |||
| Yield 5 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50, ISO 527-2 6 |
| Break 7 | 71.0 | MPa | ASTM D638 |
| Break | 71.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 8 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50, ISO 527-2 9 |
| Break 10 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Nominal strain at break | > 50 | % | ISO 527-2 11 |
| Flexural Modulus | |||
| -- 12 | 2410 | MPa | ASTM D790 |
| -- 13 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 14 | 96.5 | MPa | ASTM D790 |
| -- 15 | 97.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 16 | ||
| -30°C | 12.0 | kJ/m² | |
| 23°C | 80.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 17 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D256 |
| 23°C | 83 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 18(23°C, Total Energy) | 87.0 | J | ASTM D3763 |
| Tensile Impact Strength | 462 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 143 | °C | ASTM D648, ISO 75-2/B |
| 0.45 MPa | 144 | °C | ISO 75-2 19 |
| 1.8 MPa, Unannealed | 127 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 140 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa | 130 | °C | ISO 75-2 20 |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ASTM D1525, ISO 306/B50 8 21 |
| 50°C/h, B (50N) | 148 | °C | ISO 306 22 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| CLTE - Flow | |||
| -40 to 82°C | 6.8E-5 | cm/cm/°C | ASTM D696 |
| -- | 7.0E-5 | cm/cm/°C | ISO 11359-2 23 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | 2.0E+18 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·m | IEC 60093 24 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | |||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150, IEC 60250 25 | |
| 100 Hz | 3.00 | IEC 60250 26 | |
| Dissipation Factor | |||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150, IEC 60250 27 | |
| 100 Hz | 1.0E-3 | IEC 60250 28 | |
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 29 | UL 94 | ||
| 1.59 mm | HB | ||
| 3.20 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | HB | ISO 1210 30 | |
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 31 | |
| Glow Wire Ignition Temperature 32(2.00 mm, 5.0 sec) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index 33 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 50 mm/min |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | 50 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | 50 mm/min |
| 8 . | 50 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 50 mm/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Method I (3 point load), 2.0 mm/min |
| 13 . | 2.0 mm/min |
| 14 . | Method I (3 point load), 2.0 mm/min |
| 15 . | 2.0 mm/min |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | 3.39 m/sec |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Rate A (50°C/h), Loading 2 (50 N) |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 23 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 24 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 25 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 26 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 27 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 28 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 29 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 30 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 31 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 32 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 33 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3285 | RTP Company | ETFE | RTP |
| ASACLEAN™ EX | ASACLEAN - Sun Plastech Inc. | Proprietary | ASACLEAN™ |
| Ducaseal Static | Dugdale Plc | PVC, Flexible | Ducaseal |
| GELOY™ EXGY0070 resin | SABIC Innovative Plastics | ASA | GELOY™ |
| MAJORIS DC400 - 8229 | AD majoris | PP, Unspecified | MAJORIS |