Electrafil® J-1/CF/40
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2iw4ZL_Electrafil-J-1-CF-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®J-1/CF/40 is a polyamide 66 (nylon 66) product, which contains a 40% carbon fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Electrafil®The application fields of J-1/CF/40 include packaging, engineering/industrial accessories, automobile industry, commercial/office supplies and conveyor belts. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 28300 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 276 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.8 | % | ASTM D638 |
| Flexural Modulus (23°C) | 23400 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 407 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 263 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 257 | °C | ASTM D648 |
| CLTE - Flow | 1.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 55 | ohms | ASTM D257 |
| Volume Resistivity | 5.5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D4496: 10-100 ohmsVolume Resistivity, ASTM C611: 1-10 ohm-cmShielding Effectiveness, ES7-83, 1GHz: 30-40 dB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 277 - 288 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 282 - 293 | °C | |
| Nozzle Temperature | 282 - 288 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 79.4 - 104 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: SlowRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSH 6054 | Marco Polo International, Inc. | PS (HIPS) | MARPOL® PSH |
| TEKNIFLEX® COC PG10PG UV | Tekni-Films, a div of Tekni-Plex | Film, PETG/COC/PETG | TEKNIFLEX® |
| LubriOne™ NN-000/20T NATURAL | PolyOne Corporation | Nylon 66 | LubriOne™ |
| Sumiliteresin® PR-51494G | SBHPP | Phenolic | Sumiliteresin® |
| LNP™ THERMOCOMP™ PFW53U compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |