Diamond ABS 9501N
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Diamond ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2iIovo_Diamond-ABS-9501N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diamond ABS 9501N is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1 | ASTM D1238 | ||
| 220°C/10.0 kg | 13 | g/10 min | |
| 230°C/3.8 kg | 2.8 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, 23°C, 3.18 mm, Injection Molded) | 42.7 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 3(23°C, 3.18 mm, Injection Molded) | 2050 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm, Injection Molded | 80.0 | °C | |
| 1.8 MPa, Annealed, 3.18 mm, Injection Molded | 92.8 | °C | |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 4 |
| Thermal Index - 1.5mm | 140 | °F | UL 746B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 190 to 250 | °C | |
| Middle Temperature | 190 to 250 | °C | |
| Front Temperature | 190 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V849 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Borealis PP HE125MO | Borealis AG | PP Homopolymer | Borealis PP |
| Hifax TKC 5480X | LyondellBasell Industries | PP Copolymer | Hifax |
| Lastane 50 G/25 | LATI S.p.A. | PUR, Unspecified | Lastane |
| Karina WHITE PVC COMPOUND 750D10/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |