PLEXIGLAS® Sheet Mineral BV
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | PLEXIGLAS® Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2hrVQd_PLEXIGLAS-Sheet-Mineral-BV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PLEXIGLAS® Mineral BV is a new generation of mineral materials. The patented product PLEXIGLAS® Mineral BV (a combination of acrylic resin and mineral filler) offers unique thermoforming properties combined with a finished satin or gloss surface, in very large sizes. Like no other material before, PLEXIGLAS® Mineral BV unites the benefits of this class of material with the flexibility of PLEXIGLAS®. Owing to these properties, PLEXIGLAS® Mineral BV is suitable for both horizontal and vertical applications in indoor and outdoor areas. Indoors:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 50 - 70 | DIN EN 59 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | > 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | < 2.1 | % | ISO 527-2/1B/5 |
| Flexural Modulus | > 4700 | MPa | ISO 178 |
| Flexural Stress | > 78.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 145 - 160 | mg | DIN 14688 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.1 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 105 | °C | ISO 306/B |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | DIN 53752-A |
| Heat Deflection Temperature | 100 - 108 | °C | ISO 75-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Fire Rating | |||
| -- | B2 | DIN 4102 | |
| -- | E | EN 13501-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Impact Resistance | > 180.00 | cm | EN 483-2 |
| Distortion | Internal method | ||
| Crosswise | % | Internal method | |
| Longitudinal | % | Internal method | |
| Thickness Tolerance | 0.90 - 1.10 1.08 | cm | |
| Weight per Unit Area (8.00 mm) | 12.3 | kg/m² | |
| Forming Temperature | |||
| 2D | > 140 | °C | |
| 3D | 160 - 210 | °C | |
| Resistance to thermal cycling (hot/cold water) : No cracks, no crazing, no detachment (prEN 14688:2003) Resistance to thermal cycling (hot/cold water) : No cracks, no crazing, no detachment (ISO 19712) |
| Note Message | |
|---|---|
| 1 . | Type 1B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9135 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Tenogel® ABS A3 G20 NTLA010 AB321 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| WPP PP PPC3TF1.5-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| AGILITY™ 1001 Performance LDPE | The Dow Chemical Company | LDPE | AGILITY™ |
| TABOREN® PC 33 T 30-066 | SILON s.r.o. | PP Copolymer | TABOREN® |