Badamid® LA70 GF25 HH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2hn1EG_Badamid-LA70-GF25-HH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LA70 GF25 HH is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber. It is available in Europe. Primary attribute of Badamid® LA70 GF25 HH: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 5.3 to 6.3 | % | |
| Equilibrium, 23°C, 50% RH | 1.7 to 2.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 170 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.8 | % | ISO 527-2/5 |
| Flexural Stress (23°C) | 245 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 56 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Melting Temperature (DSC) 1 | 260 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000/50 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Nylene® 453 | Custom Resins Group | Nylon 6 | Nylene® |
| FRIANYL® B3 H V0 | Nilit Plastics | Nylon 6 | FRIANYL® |
| GAPEX® RPP20EB82HB BLACK | Ferro Corporation | PP Homopolymer | GAPEX® |
| HI-ZEX™ 530B | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |