Fasal® BIO 337
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Fasal Wood KG |
| Trademark: | Fasal® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2h2VEO_Fasal-BIO-337.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fasal BIO 337 a wood based material for injection moulding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 32.9 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Flexural Stress | 56.6 | MPa | ISO 178 |
| Flexural Strain | 3.1 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 9.6 | kJ/m² | ISO 179/1fU |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 180 | °C | |
| Nozzle Temperature | 190 | °C | |
| Mold Temperature | 20.0 - 60.0 | °C |
| Injection instructions |
|---|
| Screw speed: 30 - 50% of maximumDynamic pressure: 20% of maximumInjection pressure: approx. 30 % higherthan with plastics |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y2600T (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Telcar® TL-2585A | Teknor Apex Company | TPE | Telcar® |
| SUSTASON PPSU | Röchling Sustaplast SE & Co. KG | PPSU | SUSTASON |
| Clariant PC PC-1100H30 | Clariant Corporation | PC | Clariant PC |
| Dorlyl PVC GFD 64G | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |