Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ OCP34E compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gsMug_LNPLUBRICOMPOCP34Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* OCP34E is a compound based on PPS - Linear resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Easy Molding. Also known as: LNP* LUBRICOMP* Compound OCL-4534 EM Product reorder name: OCP34E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.39 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.080 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19000 | MPa | ASTM D638 |
| -- | 16600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 164 | MPa | ASTM D638 |
| Fracture | 159 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.6 | % | ASTM D638 |
| Fracture | 1.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 15000 | MPa | ASTM D790 |
| -- | 15300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 232 | MPa | ASTM D790 |
| -- | 236 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 390 | J/m | ASTM D4812 |
| 23°C 3 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.90 | J | ASTM D3763 |
| -- | 2.44 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 265 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 260 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMAPET® N180 | Indorama Ventures PCL | PET | RAMAPET® |
| XYRON™ X331V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| DeWAL DW 405 BNC | DeWAL Industries | UHMWPE | DeWAL |
| Karina BROWN PVC COMPOUND -E 933-36/556-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 83031-70 Brown 7460 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |