Badadur® PBT8 GF30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Bada AG |
| Trademark: | Badadur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gsInh_Badadur-PBT8-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity, 30 % glass fibres reinforced standard injection moulding grade with very good mechanical properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.37 | % | |
| Equilibrium, 23°C, 50% RH | 0.13 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 10000 | MPa | ISO 527-2 |
| Tensile Stress 2(Break, 23°C) | 140 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 2.6 | % | ISO 527-2/5 |
| Flexural Stress 4(23°C) | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength 6 | |||
| 23°C | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | kJ/m² | ISO 179/2eU |
| Notched Izod Impact Strength 7 | ISO 180/1A | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 9 | 223 | °C | ISO 3146 |
| CLTE 10 | DIN 53752 | ||
| Flow | 3.5E-5 | cm/cm/°C | |
| Transverse | 9.5E-5 | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | ||
| 20000 hrs | 140 | ||
| some hours | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity 12 | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity 13(1 MHz) | 4.10 | IEC 60250 | |
| Dissipation Factor 14(1 MHz) | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm 15 | HB | ||
| 1.60 mm 16 | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 80x10x4 mm |
| 8 . | 110x10x4 mm |
| 9 . | 10 K/min, Compound for moulding |
| 10 . | >=10x10x4 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 80x80x1 mm |
| 15 . | 125x13x.8 mm |
| 16 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Akulon® F-X9215 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Halene H HD T10S | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| Lushan PF-3 | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |
| MAJ'ECO DP364M | AD majoris | PP, Unspecified | MAJ'ECO |
| SQUARE® LIM1989-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |