POLYLAC® PA-709H
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gm8OI_POLYLAC-PA-709H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYLAC®PA-709H is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 75.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 36.0 | MPa | ISO 527-2/50 |
| Fracture | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 30 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1500 | MPa | ISO 178 |
| Flexural Stress 2 | 51.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 42 | kJ/m² | ISO 179 |
| Notched Izod Impact | 31 | kJ/m² | ISO 180/1A |
| Impact Flexural Test - Notched | 25.0 | kJ/m² | ISO 179/2C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, not annealed | 86.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ISO 306/A50 |
| -- | 106 | °C | ISO 306/A120 |
| -- | 98.0 | °C | ISO 306/B50 |
| -- | 102 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1440-UV 7C45 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| NuSil MED-4870 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| Fiberfil® J-60/20 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Geon™ Vinyl Rigid Extrusion L0248 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| LNP™ THERMOCOMP™ RF003H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |