UmaPET COMH Datasheet,PET,Ester Industries Ltd.-SHANGHAI SUSHENG

Message
KEY FEATURES UmaPET COMH is high barrier metallized film, metallized on plain surface with plasma other side corona treated. It exhibits good barrier properties along with good metal to film bond strength/adhesion. It has excellent mechanical properties, flex crack resistance and excellent gloss. APPLICATIONS UmaPET COMH is used as sandwich barrier layer in flexible packaging applications which require good barrier and good bond strength in laminates. Typical usage as barrier layer in laminates for confectionary, milk powder, cereals, snacks, chips, extruded foods, tea etc.

General Information
Features	Barrier Resin Bondability Good Adhesion Good Crack Resistance High Gloss Metallizable
Uses	Film Laminates Packaging
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0100 mm	2.5	%
Flow : 150°C, 30 min, 0.0120 mm	2.5	%
Flow : 150°C, 30 min, 0.0150 mm	2.5	%
Flow : 150°C, 30 min, 0.0230 mm	2.5	%
Across Flow : 150°C, 30 min, 0.0100 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0150 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0230 mm	0.40	%
Surface Tension			ASTM D2578
Corona Side : 10.0 µm	54	mN/m
Corona Side : 12.0 µm	54	mN/m
Corona Side : 15.0 µm	54	mN/m
Corona Side : 23.0 µm	54	mN/m
Metallized side : 10.0 µm	56	mN/m
Metallized side : 12.0 µm	56	mN/m
Metallized side : 15.0 µm	56	mN/m
Metallized side : 23.0 µm	56	mN/m

Films	Nominal Value	Unit	Test Method
Yield			Internal Method
10.0 µm	71.4	m²/kg
12.0 µm	59.5	m²/kg
15.0 µm	47.6	m²/kg
23.0 µm	31.0	m²/kg

Optical	Nominal Value	Unit	Test Method
Optical Density			Internal Method
10.0 µm	-2.4 to 7.6	%
12.0 µm	-2.4 to 7.6	%
15.0 µm	-2.4 to 7.6	%
23.0 µm	-2.4 to 7.6	%

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	10 12 15 23	µm
Film Thickness - Recommended / Available	10, 12, 15, 23 µm
Tensile Strength			ASTM D882
MD : Break, 10 µm	206	MPa
MD : Break, 12 µm	206	MPa
MD : Break, 15 µm	186	MPa
MD : Break, 23 µm	186	MPa
TD : Break, 10 µm	216	MPa
TD : Break, 12 µm	216	MPa
TD : Break, 15 µm	206	MPa
TD : Break, 23 µm	206	MPa
Tensile Elongation			ASTM D882
MD : Break, 10 µm	100	%
MD : Break, 12 µm	100	%
MD : Break, 15 µm	100	%
MD : Break, 23 µm	100	%
TD : Break, 10 µm	90	%
TD : Break, 12 µm	90	%
TD : Break, 15 µm	90	%
TD : Break, 23 µm	90	%
Oxygen Permeability ¹			ASTM D3985
23°C, 10 µm	0.800	cm³/m²/24 hr
23°C, 12 µm	0.700	cm³/m²/24 hr
23°C, 15 µm	0.700	cm³/m²/24 hr
23°C, 23 µm	0.700	cm³/m²/24 hr
Water Vapor Transmission			ASTM F1249
-- ²	0.40	g/m²/24 hr
-- ³	0.40	g/m²/24 hr
-- ⁴	0.50	g/m²/24 hr
-- ⁵	0.40	g/m²/24 hr

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	2gVQKx_UmaPET-COMH.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
MAXAMID™ PA6G25-BK10	Pier One Polymers, Inc.	Nylon 6	MAXAMID™
Spartech Polycom PP6120 B38	Spartech Polycom	PP, Unspecified	Spartech
Synthos EPS® 0822F/CZ	Synthos S.A.	PS (EPS)	Synthos EPS®
LUVOCOM® 1/GK/30/TF/13/SI/2	Lehmann & Voss & Co.	Nylon 66	LUVOCOM®
MAJORIS DT360 - 8229	AD majoris	PP, Unspecified	MAJORIS