SABIC® HDPE F00952
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2g5aFo_SABIC-HDPE-F00952.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® HDPE F00952 resin is a high molecular weight high density polyethylene copolymer which has been designed specifically for blown film extrusion. Its high molecular weight, broad molecular distribution and high density combine succesfully to give excellent extrudability with high film strength and rigidity. The material contains anti oxidant . |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.050 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 9.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 15 µm, blown film | 1250 | MPa | ASTM D882 |
| TD : 15 µm, blown film | 1500 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 15 µm, blown film | 33.0 | MPa | ASTM D882 |
| TD : Yield, 15 µm, blown film | 31.0 | MPa | ASTM D882 |
| MD : Broken, 15 µm, blown film | 60.0 | MPa | ASTM D882 |
| TD : Broken, 15 µm, blown film | 56.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 15 µm, blown film | 400 | % | ASTM D882 |
| TD : Broken, 15 µm, blown film | 550 | % | ASTM D882 |
| Dart Drop Impact (15 µm, Blown Film) | 180 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15 µm, blown film | 12 | g | ASTM D1922 |
| TD : 15 µm, blown film | 60 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 235 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tufpet PBT G2820 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| Adell Polyamide BJ-14 Glass Reinforced High Impact | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| APEX® 80-C440-C | Teknor Apex Company | PVC, Flexible | APEX® |
| Fainplast PVC GS 100/2 | Fainplast Compounds S.r.l | PVC, Semi-Rigid | Fainplast PVC |
| OPNYL OP66GF60 | Ovation Polymers Inc. | Nylon 66 | OPNYL |