Borealis PP RA130E-2492
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2fwB6T_Borealis-PP-RA130E-2492.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RA130E-2492 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is dark blue coloured. The product is used for single as well as for multilayer pipes, where you then differentiate between plastic multilayer and aluminium multilayer pipes. RA130E-2492 is intended to fulfill following standards and regulations, in case of appropriate industrial manufacturing standard procedures applied and a continuous quality system is implemented.
The pipe system will show high durability, no corrosion, good weldability, homogeneous joints, low tendency to incrustrations and fast and easy installation. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 14 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | ISO 179/1eA |
| 0°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | ISO 179/1eU |
| 0°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (0 to 70°C) | 1.5E-4 | cm/cm/°C | DIN 53752 |
| Thermal Conductivity | 0.24 | W/m/K | DIN 52612 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 210 | °C | |
| Cylinder Zone 2 Temp. | 180 - 210 | °C | |
| Cylinder Zone 3 Temp. | 180 - 210 | °C | |
| Cylinder Zone 4 Temp. | 180 - 210 | °C | |
| Cylinder Zone 5 Temp. | 180 - 210 | °C | |
| Melt Temperature | 210 - 220 | °C | |
| Die Temperature | 210 - 220 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 210 to 220°C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 485N | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| NYLOY® UB-0010N C40N2B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| NYLEM® 66 FR V0 | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| Karina IVORY PVC COMPOUND -E 70900-35/ 1-E-AC (AS80NF)/K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST EP 4030HG38 | Ester Industries Ltd. | PBT | ESTOPLAST EP |