ESTAPROP H 10100 BS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Cossa Polimeri S.r.l. |
| Trademark: | ESTAPROP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2fgO2f_ESTAPROP-H-10100-BS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ESTAPROP H 10100 BS is a Polypropylene Homopolymer (PP Homopolymer) product filled with 50% mineral. It is available in Europe. Typical application: Packaging. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 25.0 | MPa | |
| Break | 21.0 | MPa | |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 15 | J/m | |
| 0°C | 25 | J/m | |
| 23°C | 30 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8948-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Elastollan® 560 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| E-RIALFILL H 15 20 T | RIALTI Srl | PP Homopolymer | E-RIALFILL |
| KOPA® KN173HI3R | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Lotader® 3430 | Arkema | EMA | Lotader® |