BJB Polyurethane TC-312 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2fEzTk_BJB-Polyurethane-TC-312-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The TC-312 A/B polyurethane foam system is a rigid, closed cell foam with a density of 12 lbs. per cubic foot. The TC-312 can be easily mixed by hand in small batches using a rapid, vigorous mixing action or by using a Jiffy Mixer® in a drill to provide a high-shear mix in small to large quantities. For low to high production, this foam system can also be machine dispensed using BJB's Centerpointe Meter-Mix equipment. Cured parts can be sanded, stapled, painted or stained within a short time after demolding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Part A | 1.227 | g/cm³ | |
| Part B | 1.247 | g/cm³ | |
| K (wear) Factor (25°C) | 0.285 | ASTM C518 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cream Time | 30.0 to 40.0 | sec | |
| Demold Time | 15.0 to 20.0 | min | |
| Rise Time | 1.5 to 2.0 | min | |
| Tack Free Time | 3.0 to 4.0 | min |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brookfield Viscosity | |||
| Part A : 25°C | 250 | mPa·s | |
| Part B : 25°C | 2160 | mPa·s |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Closed Cell Content | 98 | % | ASTM D2856 |
| Free Rise Foam Density | 5400 | g |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 2.90 | MPa | ASTM D1623 |
| Flexural Strength | 3.62 | MPa | ASTM D790 |
| Compressive Strength | 3.28 | MPa | ASTM D1621 |
| Shear Strength | 2.24 | MPa | ASTM C273 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 80 | ||
| Part B | Mix Ratio by Weight: 100 | ||
| Shelf Life | 26 | wk |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA66 A2G6304 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| Borealis PP HD621CF | Borealis AG | PP Homopolymer | Borealis PP |
| Electrafil® 02010 MB | Techmer Engineered Solutions | PP, Unspecified | Electrafil® |
| POLYAXIS® PD 3000 | A. Schulman Inc. | PP Copolymer | POLYAXIS® |
| Osterlene® PPC35-2 | Osterman & Company | PP Impact Copolymer | Osterlene® |