Polycomp® PDR CB 08
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Polycomp® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2eaPTf_Polycomp-PDR-CB-08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCOMP PDR CB 08 is a medium to high flow, high crystaline unfilled polypropylene copolymer. It has been developed for applications requiring increased rigidty and good impact strength while maintaining the good surface appearance and low SG of an unfilled material. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 to 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 104 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 76 | ||
| Shore D, 15 sec, 3.00 mm | 68 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 150 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 1610 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 76 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 1200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 127 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209 Z | RTP Company | Nylon 66 | RTP |
| Xuchuan 2006/B-8016 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| GLAMIDE® T-602G30 | TOYOBO America, Inc. | PARA | GLAMIDE® |
| Karina NATURAL PVC COMPOUND 70900-25/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8220-65 Grey 9553 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |