Order Products : sales@su-jiao.com
Axiall PVC MP-6510
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | Axiall PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2eZExM_Axiall-PVC-MP-6510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Georgia Gulf MP-6510 is a maximum properties electrical grade PVC injection molding compound possessing excellent strength and toughness. In addition, it has good processing stability and surface appearance. It carries a UL 94 V-0/5VA flammability rating, as well as a UL RTI rating. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2480 | MPa | ASTM D638 |
| Tensile Strength | 41.4 | MPa | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.18 mm | 160 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 960 | J/m | ASTM D256 |
| Dart Drop Impact 1(23°C) | 22.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 75.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| RTI Elec (1.40 mm) | 90.0 | °C | UL 746 |
| RTI Imp (1.40 mm) | 85.0 | °C | UL 746 |
| RTI (1.40 mm) | 90.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 5VA | UL 94 | |
| Oxygen Index | 36 | % | ASTM D2863 |
| Additional Information |
|---|
| Flow Ratio (Distance/Wall Thickness), Georgia Gulf Test Method, 390-400°F: 180 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Shot Size | 35 - 75 | % | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 163 | °C | |
| Middle Temperature | 174 - 191 | °C | |
| Front Temperature | 182 - 193 | °C | |
| Nozzle Temperature | 177 - 193 | °C | |
| Processing (Melt) Temp | 202 - 210 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 82.7 - 138 | MPa | |
| Holding Pressure | 48.3 - 82.7 | MPa | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 25 - 80 | rpm | |
| Clamp Tonnage | 3.4 | kN/cm² | |
| Screw L/D Ratio | 16.0:1.0 to 24.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Method f, geometry FB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravaflex CIIR | Ravago Group | CIIR | Ravaflex |
| RheTech Polypropylene CC40P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| SEPAZ™ LA30 | Mando Advanced Materials Co., Ltd. | Nylon 66 | SEPAZ™ |
| Moplen HP400M | LyondellBasell Industries | PP, Unspecified | Moplen |
| Sylvin 7011EE-75 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |