Bayflex® MP-10000
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2dq0ir_Bayflex-MP-10000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bayflex MP-10,000 is a solid elastomer which has a flexural modulus of approximately 10,000 psi (69 MPa) at room temperature. It is processed on reaction injection molding (RIM) equipment and is used for rollers, gaskets, and encapsulated windows. This system combines rapid demold times, excellent integrity at demold, improved release characteristics, and outstanding physical properties. Bayflex MP-10,000 is a formulated RIM system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol. As with any product, use of the Bayflex MP-10,000 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.998 | g/cm³ | ASTM D792 |
| -- | 1.00 | g/cm³ | ASTM D1622 |
| Molding Shrinkage - Flow (3.00 mm) | 1.4 | % | Internal method |
| Water Absorption (24 hr, 3.00 mm) | 3.3 | % | Internal method |
| Water absorption rate- 240 hr (3.00 mm) | 5.0 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Temperature Brittleness (-50°C, 3.00 mm) | No Cracking | ASTM D746 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Immersion, Length Increase | 1.4 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 3.00mm | 90 | ASTM D2240 | |
| Shaw D, 3.00mm | 40 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 3.00 mm) | 15.2 | MPa | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -30°C, 3.00 mm | 163 | MPa | ASTM D790 |
| 23°C, 3.00 mm | 68.9 | MPa | ASTM D790 |
| 65°C, 3.00 mm | 54.5 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 20% strain 1 | 4.14 | MPa | ASTM D412 |
| 50% strain, 3.00mm 2 | 5.17 | MPa | ASTM D412 |
| 100% strain, 3.00mm 3 | 6.89 | MPa | ASTM D412 |
| Tensile Strength (Break, 3.00 mm) | 15.2 | MPa | ASTM D412 |
| Tensile Elongation (Break, 3.00 mm) | 300 | % | ASTM D412 |
| Tear Strength 4(3.00 mm) | 42.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (3.00 mm) | 1.7E-4 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components 5 | |||
| Component a | Mixing ratio by weight: 38 | ||
| Component B | Mixing ratio by weight: 100 | ||
| Demold Time | 0.50 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Part A Type: Isocyanate Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 700 mPa-s Flash Point PMCC: 213 °C Part B Type: Polyol Specific Gravity @ 25°C: 1.03 Viscosity @25°C: 1350 mPa-s Flash Point PMCC: 185 °C Molding Parameters Material Temperature: 32 to 42 °C Mold Temperature: 65 to 70 °C |
| Note Message | |
|---|---|
| 1 . | Die C, 510 mm/min |
| 2 . | C mold, 510mm/min |
| 3 . | Mouth die C, 510mm/min |
| 4 . | C mould |
| 5 . | 105 Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SL704M3T | RJM International, Inc. | PP, Unspecified | RJM |
| Yanshan PE 7000F | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| Nipol® LX513 | Zeon Corporation | Latex | Nipol® |
| Ferro PP TPP30AD69BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Sylvin 8225-90FUV Yellow 4217 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |