Rotec® AES A 711
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® AES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2d0Ma5_RotecAESA711.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rotec®AES A 711 is an acrylonitrile ethylene styrene (AES) material,. This product is available in Europe, and the processing method is injection molding. Rotec®The main features of AES A 711 are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 33 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 44.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 30 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 78.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 96.0 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL4F 802 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Cheng Yu T888G15 | Cheng Yu Plastic Company Limited | PBT | Cheng Yu |
| K-Prene GHT 65 | Technovinyl Polymers India Ltd. | TPE | K-Prene |
| Latimass 62-07 D025 | LATI S.p.A. | Nylon 6 | Latimass |
| POLYFLON™ F-104 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |