Padermid 6 GF30 N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TKC Kunststoffe e.K. |
| Trademark: | Padermid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2cZ91l_Padermid-6-GF30-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Padermid 6 GF30 N is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in Europe for injection molding. Important attributes of Padermid 6 GF30 N are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage | STN 64 0808 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.45 | % | |
| Moisture Absorption (23°C) | 1.8 | % | DIN 53495 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature | 200 | °C | ISO 306 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | < 0.15 | % | DIN 53495 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8900 | MPa | ISO 527-2 |
| Tensile Stress | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7600 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 11 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 55 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 210 | °C | ISO 306/B |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 8.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 5.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 575 | V | STN 34 6468 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titacon® GF525 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Homopolymer | Titacon® |
| Nylene® NX3024F | Custom Resins Group | Nylon 6 | Nylene® |
| Badamid® A702 GF25 FR HF | Bada AG | Nylon 66 | Badamid® |
| LNP™ LUBRICOMP™ RFL46 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Sumiliteresin® PR-F-116 | SBHPP | Phenolic | Sumiliteresin® |