ALCOM® AWL 10/3 WT1308-05LB
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® AWL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2cGDAF_ALCOM-AWL-10-3-WT1308-05LB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® AWL 10/3 WT1308-05LB is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Applications of ALCOM® AWL 10/3 WT1308-05LB include automotive, lighting applications and reflectors. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 40.0 | MPa | |
| -- | 35.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 2.0 | % | |
| Break | 5.0 | % | |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% Strain | 60.0 | MPa | |
| -- | 60.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 10 | kJ/m² | |
| -40°C | 4.0 | kJ/m² | |
| -20°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 50 | kJ/m² | |
| -20°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 650 | °C | |
| 2.00 mm | 650 | °C | |
| 3.00 mm | 650 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 84 | % | DIN 5033 |
| Y10 of Transmittance : 500.0 µm | 0.20 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Circulation Dryer | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| Circulation Dryer | 3.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILAMID® A3 W GF30 | Nilit Plastics | Nylon 66 | NILAMID® |
| Fluon® PFA P-66P | Asahi Glass Co., Ltd. | PFA | Fluon® |
| Hylon® N1000L2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Karina GRAY COLOR CONCENTRATE 18/ 97-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OPTUM® DPP40WI08GY | Ferro Corporation | Polyolefin, Unspecified | OPTUM® |