Iupilon® EFD2110U
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2bzgQg_Iupilon-EFD2110U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupilon® EFD2110U is a Polycarbonate (PC) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupilon® EFD2110U: Flame Rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 4.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption (Saturation, 23°C) | 0.24 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 100 | % | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 92.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 136 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 6.5E-5 | cm/cm/°C | |
| Transverse | 6.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.20 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 270 to 300 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 1500H (S30G) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Borealis PP EE002AE | Borealis AG | PP, Unspecified | Borealis PP |
| Escorene™ Ultra LD 755 Series | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| LENTICULAR® 60LPI-3D | Polycasa | PETG | LENTICULAR® |
| LNP™ STAT-KON™ DD0001 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |