PRL PPX-GP5
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2bswpE_PRL-PPX-GP5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-GP5 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 2.0 to 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 62.1 | MPa | |
| Break, 3.18 mm | 60.0 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 35 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2380 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 97.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1 |
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 130 | J/m | |
| 23°C, 3.18 mm | 210 | J/m | |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 132 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 127 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 271 to 310 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ SC-253 | Idemitsu Kosan Co., Ltd. | PC+ABS | TARFLON™ |
| Karina CLEAR PVC COMPOUND 78/200-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SD POLYCA™ CR3241 | Sumika Styron Polycarbonate Limited | PC+PET | SD POLYCA™ |
| Sylvin 9600-55 Green 3108 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Kepital® TS-25H | KEP Americas | Acetal (POM) Copolymer | Kepital® |