Kepamid® 1515SM7
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2azNzO_Kepamid-1515SM7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kepamid® 1515SM7 is a Polyamide 6 (Nylon 6) material filled with 15% mineral. It is available in Asia Pacific, Europe, or North America. Important attributes of Kepamid® 1515SM7 are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 to 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 63.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 8.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4120 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 190 | °C | |
| 1.8 MPa, Unannealed | 105 | °C | |
| Melting Temperature | 220 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content 1 | 15 | % | ASTM D5630 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Furnace |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3709 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tenac™-C CF454 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| UBE Nylon 1018I | UBE Industries, Ltd. | Nylon 6 | UBE Nylon |
| CP PRYME® Nylon 66 NN133TL | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| KOCETAL® K200 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |