| Polyamide 66 reinforced with 30% glass fibre, flame retardant an UL 94 V0 at 1.6 mm rating. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.56 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 6.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | 90 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | |||
| Yield | 130 | 80.0 | MPa | |
| Break | 130 | 80.0 | MPa | |
| Tensile Elongation 2(Break) | 2.0 | 3.5 | % | ASTM D638 |
| Flexural Modulus 3 | 9500 | 6000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 160 | 110 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -20°C, 3.20 mm | 50 | 70 | J/m | |
| 23°C, 3.20 mm | 70 | 90 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 245 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 260 | -- | °C | ASTM D3418 |
| CLTE - Flow | 4.0E-6 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 30 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Delta N66R-4G70 | Delta Polymers | Nylon 66 | Delta |
| Formolene® 3355O | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| LNP鈩?THERMOCOMP鈩?PX85100 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| LUVOCOM® 80-8003 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Pier One POM AH500P-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | Pier One POM |