Nylfor® A2 MF/25 H1 NATURALE
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Nylfor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2YZwO8_Nylfor-A2-MF-25-H1-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66/6, 25% mineral filled, heat and UV stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 285 | °C | |
| Front Temperature | 300 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ WS-53NF | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Globalprene® 1440F | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Karina IVORY PVC COMPOUND 105909-35/ 1-DY-ACE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-LOY™ 9X05426C compound | SABIC Innovative Plastics | Acrylic (PMMA) | LNP™ STAT-LOY™ |
| SABIC® FORTIFY™ C3070D | Saudi Basic Industries Corporation (SABIC) | TPO (POE) | SABIC® FORTIFY™ |