CERTENE™ LLHC-318A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2YUabQ_CERTENE-LLHC-318A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLHC-318A is a certified prime, Ethylene-Hexene Copolymer developed for extrusion of Cast Films needing a combination of excellent processability and very good stiffness and toughness. LLHC-318A applications include general purpose cast films, stretch wrap and packaging films. LLHC-318A contains No slip and No antiblock. LLHC-318A complies with FDA regulation 21CFR 177.1520(c) 3.1a, (except for articles used for the packing or holding of food during cooking). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 20 µm | 114 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm | 124 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 8.14 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 7.58 | MPa | ASTM D882 |
| MD : Break, 20 µm | 65.2 | MPa | ASTM D882 |
| TD : Break, 20 µm | 38.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 550 | % | ASTM D882 |
| TD : Break, 20 µm | 800 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 80 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 200 | g | ASTM D1922 |
| TD : 20 µm | 700 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.3 µm) | 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 0.8 mil (20 µm) cast film; melt temperature 550°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A RELY 5924R 10000 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| UBE Nylon 7034 T | UBE Engineering Plastics, S.A. | Nylon 612 | UBE Nylon |
| ALCOM® PA66 910/1 MO2 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Hanwha Total PP HJ730L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| POLYVIN® Polyvin SNP 0501- | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |