Rilsan® CLEAR G 850 Rnew L
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Xu6FY_Rilsan-CLEAR-G-850-Rnew-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® Clear G850 Rnew L is a high performance transparent polyamide having outstanding purity level and partially based on renewable resources. This grade has been specially designed for high quality optical lens applications, such as non corrective sun lenses or reading glasses. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 40°C, 24 hr, 2.00 mm | 0.75 | % | |
| Flow : 40°C, 24 hr, 2.00 mm | 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 4.0 | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 80 | ||
| Shore D, 15 sec | 78 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1670 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 61.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 8.0 | % | |
| Break | > 100 | % | |
| Flexural Modulus | 1630 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Glass Transition Temperature | 150 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm, 560 nm) | 91.7 | % | ASTM D1003 |
| Refractive Index | 1.5030 | ISO 489 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 45 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 300 | °C | |
| Mold Temperature | 20.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SolVin 264GC | INOVYN | PVC, Unspecified | SolVin |
| Cheng Yu N6G15 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| DJSilicone NE-7250 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Escorene™ Ultra AD 0433EH2 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| LNP™ THERMOCOMP™ ZF006 compound | SABIC Innovative Plastics | PPE+PS | LNP™ THERMOCOMP™ |