Tecomid® NA40 NL IH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecomid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Wvaau_Tecomid-NA40-NL-IH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6.6, impact modified, natural |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 1.7 | % | Internal method |
| Flow direction | 1.7 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | % | ISO 62 |
| Moisture Content | % | ISO 960 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 25 | kJ/m² | ISO 180/1A |
| 23°C | 85 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 50.0 - 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa |
| Injection instructions |
|---|
| Pre-drying is not necessary for materials in moisture proof closed bags. |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 16MA400 | Reliance Industries Limited | LDPE | RELENE® |
| SCHULAMID® 6GF30 | A. Schulman Inc. | Nylon 6 | SCHULAMID® |
| Stamylex® 1066 F | Borealis AG | LDPE | Stamylex® |
| Formolene® 6730J | Formosa Plastics Corporation, U.S.A. | PP Copolymer | Formolene® |
| Rotuba CAB B900 (16% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |