LNP™ THERMOCOMP™ AF002XXC compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2W6FVc_LNP-THERMOCOMP-AF002XXC-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* AF002XXC is a compound based on ABS resin containing 10% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound AF-1002 HP Product reorder name: AF002XXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.38 | % | ISO 294-4 |
| Flow : 24 hr | 0.41 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.38 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4140 | MPa | ASTM D638 |
| -- | 4200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 66.9 | MPa | ASTM D638 |
| Break | 64.9 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.5 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4210 | MPa | ASTM D790 |
| -- | 4500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 106 | MPa | ASTM D790 |
| -- | 108 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 2 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 320 | J/m | ASTM D4812 |
| 23°C 3 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.3 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 102 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 92.8 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 95.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K2051 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Devlon PVC | Devol® Engineering Polymers | PVC, Unspecified | Devlon |
| Dynacom CRT-140 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| Kingfa PET-RG15 | Kingfa | PET | Kingfa |
| StarMed® 9030-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMed® |