POLIGOM GO/12 R
| Category: | EPDM , Ethylene Propylene Diene Terpolymer |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | POLIGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2VtYwK_POLIGOM-GO-12-R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLIGO is the trade-mark of our crosslinkable EPDM compound. POLIGOM GO/12 R is a chemically crosslinkable OIL RESISTANT rubber for power cables insulation and sheathing. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 PSF or MAC/203 HS. REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 98/2 Certify: HD22.1 EM2, BS7655 RS4 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 12.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | > 300 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (70°C, 240 hr) | < 15 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (70°C, 240 hr) | < 15 | % | IEC 60811 |
| Change in Tensile Strength (100°C, 24 hr, in mineral oil) | < 40 | % | IEC 60811 |
| Change in Tensile Strain at Break (100°C, 24 hr, in mineral oil) | < 40 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 200°C | % | IEC 60811 | |
| Residual : 200°C | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | BS 6622 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 175 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Cylinder Zone 5 Temp. | 220 | °C | |
| Die Temperature | 225 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin in hot water at 85/90°C for two hours (up to 1/1,5 mm thickness) Steam treatment at 0,15 bar for 5/6 hours. Ambient crosslink is possible on sufficient time that depend from air temperature and relative moisture. |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR PP FR 7A11 | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| 4MID® 9B22125 H | 4Plas | Nylon 6 | 4MID® |
| Ateva® 2842A | Celanese EVA Performance Polymers | EVA | Ateva® |
| LUVOCOM® 1105-8160 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| THERMORUN® Z103B/N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |