LEXAN™ 3413R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2VW28I_LEXAN-3413R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GR, provides improved mechanical properties and UL94V-1 rated at 0.058". Internal mold release added. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.43 | g/cm³ | |
| -- | 1.44 | g/cm³ | |
| Specific Volume | 0.697 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 300°C/1.2 kg | 5.0 | g/10 min | |
| 300°C/5.0 kg | 19 | g/10 min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | Internal Method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.14 | % | |
| Equilibrium, 23°C | 0.26 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 92 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 100 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 6610 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 153 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 24.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 5.00 | J | ASTM D3029 |
| Tensile Impact Strength 5 | 67.0 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 151 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 146 | °C | |
| Vicat Softening Temperature | 165 | °C | ASTM D1525 6 |
| CLTE - Flow (-40 to 95°C) | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1130 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.35 | ||
| 60 Hz | 3.35 | ||
| 1 MHz | 3.31 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.1E-3 | ||
| 60 Hz | 1.1E-3 | ||
| 1 MHz | 7.0E-3 | ||
| Arc Resistance 7 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 5 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.47 mm | V-1 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Type S |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicoflex 100O | Ravago Group | ABS | Sicoflex |
| Dorlyl PVC GFC 65E | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |
| Geon™ Vinyl Flexible C6500 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 916VO-85UV Yellow 4184 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Novalloy-B B2703 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |