Latilub 73/13-15T G/15
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2VGL8U_Latilub-73-13-15T-G-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Polyoximethylene (POM). PTFE. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.3 to 1.6 | % | |
| Flow : 2.00 mm | 0.70 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.8 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.19 | ||
| vs. Itself - Static | 0.25 | ||
| Wear Factor | 450 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 155 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 175 to 200 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 508 | Marco Polo International, Inc. | HDPE | MARPOL® |
| SCHULADUR® A3 GF 30 K2224 | A. Schulman Europe | PBT+ASA | SCHULADUR® |
| Next ABS SX-02BK | Next Polymers Ltd. | ABS | Next ABS |
| Badaflex® TPE-S 40A 1000 | Bada AG | TPE | Badaflex® |
| Lucent TPO TPO-20T | Lucent Polymers, Inc. | Polyolefin, Unspecified | Lucent TPO |