Monprene® OM-10250
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2U1aWz_Monprene-OM-10250.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene OM-10250 is designed for overmolding applications like grips and anti-skid parts for consumer products. Monprene OM-10250 is an opaque grade that exhibits excellent adhesion to PC, ABS, and PC/ABS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 54 | ASTM D2240 | |
| Shaw A, 5 seconds | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 1.98 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 2.16 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 3.17 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 3.58 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 5.27 | MPa | ASTM D412 |
| Flow : Fracture | 4.63 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 620 | % | ASTM D412 |
| Flow : Fracture | 520 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 27.7 | kN/m | ASTM D624 |
| Flow | 26.8 | kN/m | ASTM D624 |
| Compression Set 8 | ASTM D395B | ||
| 23°C, 22 hr | 25 | % | ASTM D395B |
| 70°C, 22 hr | 86 | % | ASTM D395B |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 138 - 188 | °C | |
| Middle Temperature | 154 - 199 | °C | |
| Front Temperature | 154 - 216 | °C | |
| Nozzle Temperature | 154 - 221 | °C | |
| Processing (Melt) Temp | 166 - 221 | °C | |
| Mold Temperature | 10.0 - 32.2 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Moisture can degrade the material. Drying is suggested. This can be accomplished by placing the material in a desiccant dryer for 2 to 4 hours at140°F. |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 140 LF | RTP Company | PP, Unspecified | RTP |
| Unipren® Elastomers A3 PRTA010 80A EM06S1 UP336 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Chiao Fu PA6 MC312LST BK | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| KOCETAL® GF105 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Plaskon NXG-1LAR | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |