TORZEN® GT3300HSL BK20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2TwkHo_TORZEN-GT3300HSL-BK20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® GT3300HSL BK20 is a 33% glass reinforced, impact modified, heat stabilized, black, PA66 resin suitable for many injection molding applications where high tensile strength and dimensional stability are needed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Flow : 2.00 mm | 0.30 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.1 | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 7900 | MPa | ISO 178 |
| Flexural Stress | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 15 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 247 | °C | ISO 75-2/A |
| Melting Temperature | 262 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 to 0.18 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 1.00 | MPa | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent Depth | 7.0E-3 to 0.040 | mm | |
| Screw Speed | Low rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NBX0 HF75 NL | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Chemlon® 104-13 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® GS710060 | LyondellBasell Industries | LLDPE | Petrothene® |
| Plexiglas® Resist zk6HF | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |