Vyncolit庐 3520CG
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2TVklt_Vyncolit-3520CG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® 3520CG is a graphite filled phenolic molding compound used for low friction applications where dimensional stability is required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Apparent Density | 0.86 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | 0.54 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Post Shrinkage | 0.11 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.68 | % | ISO 178 |
| Tensile Modulus (Injection Molded) | 16000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 54.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.39 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 13000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 83.0 | MPa | ISO 178 |
| Compressive Stress | 161 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 1.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 3.1 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.6 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 2.0E-5 | cm/cm/°C | TMA |
| Lateral | 3.1E-5 | cm/cm/°C | TMA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron H2255 | TECTRON Systems Pte Ltd | TPV | Tectron |
| THERMORUN® Z101N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| TRISTAR® PC-10FR-(V18) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Algoflon® L101 | Solvay Specialty Polymers | PTFE | Algoflon® |
| LUBEMIX 65 BLACK | LUBEN PLAST srl | PC+ABS | LUBEMIX |