CALP 1100G-1
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | CALP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2T1YTF_CALP-1100G-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CALP 1100G-1 is a Polyolefin product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: impact resistant. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 1.4 | % | |
| Across Flow : 2.00 mm | 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 77 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 19.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Flexural Modulus | 1870 | MPa | ASTM D790 |
| Flexural Strength | 33.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 111 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-2021GR | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Sanren F500EPS (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| HiFill® PSU/ABS 1000 | Techmer Engineered Solutions | PSU | HiFill® |
| PANDEX 727 | DIC Corporation | PUR, Unspecified | PANDEX |
| PARAPET GR01270 | Kuraray Co., Ltd. | Acrylic (PMMA) | PARAPET |