MOSTEN MB 720
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | UNIPETROL RPA |
| Trademark: | MOSTEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2S641f_MOSTEN-MB-720.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene Mosten MB 720 is a block copolymer, intended for injection moulding of parts requiring very high impact strength. Typical application is production of various technical parts, containers and boxes, crates (clap-boxes), etc. Mosten MB 720 can also be used for compounding of products, especially for automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 100 | % | ISO 527-2 |
| Flexural Modulus | 1050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 52.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 MF UV RUB0032 PC322 MSP | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| POLYTROPE® STR 1032EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| Taitacell EPS 321LF | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| JSR EPR EP01P | JSR Corporation | EPDM | JSR EPR |
| ULTEM™ 1000E resin | SABIC Innovative Plastics | PEI | ULTEM™ |