Geon™ Vinyl Flexible FC900
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Flexible |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2RtLGa_Geon-Vinyl-Flexible-FC900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon™ Vinyl Flexible FC900 is a Flexible Polyvinyl Chloride product. It can be processed by extrusion or injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1(Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 15.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 330 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -24.0 | °C | ASTM D746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 191 to 196 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 188 to 193 | °C |
| Note Message | |
|---|---|
| 1 . | Inst. Hardness +/- 5 units. |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA6 D83 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| Xuchuan 1003/B-5301 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyether | Xuchuan |
| Fainplast PVC GK 91 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KOPA® KN173HI4 | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| TORZEN® HV125A NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |