LNP™ COLORCOMP™ GX02708 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Q0t1x_LNPCOLORCOMPGX02708compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* COLORCOMP* GX02708 is an unfilled Polysulfone resin. Added feature of this grade is: Healthcare. Also known as: LNP* COLORCOMP* Compound PDX-G-02708 HC Product reorder name: GX02708 |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 174 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.60 mm) | 130 | kV/mm | ASTM D149 |
| Dissipation Factor (1 MHz) | 6.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 - 338 | °C | |
| Middle Temperature | 338 - 349 | °C | |
| Front Temperature | 349 - 360 | °C | |
| Processing (Melt) Temp | 360 - 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C HC450 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| XANTAR® C CM 506 U | Mitsubishi Engineering-Plastics Corp | PC+ABS | XANTAR® C |
| DynaMix™ 2035-LM | Polymer Dynamix | Nylon 66 | DynaMix™ |
| Emulprene® 1013A | INSA | SBR, Emulsion | Emulprene® |
| Moplen EP542R | PolyMirae | PP Impact Copolymer | Moplen |