TECHNYL® C 52G1MX 25 GREY 7035
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2PwrcZ_TECHNYL-C-52G1MX-25-GREY-7035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant polyamide PA6 reinforced with mineral filler for injection moulding, also suitable for thin wall parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Molding Shrinkage - Flow | ||||
| -- | 1.1 | -- | % | ISO 294-4 |
| -- | 0.75 | -- | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6130 | 4000 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 70.0 | 55.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.0 | 4.0 | % | ISO 527-2/1A |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-30°C) | 30 | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | -- | 3.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 28 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- | ||
| 3.20 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 700 | -- | °C | |
| 1.60 mm | 725 | -- | °C | |
| Oxygen Index | 29 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 2230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F200A (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Sindustris PBT GP2307FS | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Unichem 9614 | Colorite Polymers | PVC, Unspecified | Unichem |
| Indothene LL 36RA045 | Reliance Industries Limited | LLDPE | Indothene LL |
| InnoFR™ FX-8071 | Innovative Polymers, Inc. | TSU | InnoFR™ |