RTP 6091-85A BLACK
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2Psg9M_RTP-6091-85A-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA-6 bondable - manufactured with Santoprene™ TPV technology |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Moisture Content | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 85 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 4.41 | MPa | ASTM D412 |
| Tensile Strength 2(Break) | 7.24 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 400 | % | ASTM D412 |
| Tear Strength 4 | 28.9 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 70°C, 22 hr | 50 | % | ASTM D395B |
| 125°C, 22 hr | 69 | % | ASTM D395B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 263 - 282 | °C | |
| Mold Temperature | 35.0 - 71.1 | °C |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | C mould |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-93A-B30 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| VITAMIDE® AR76GR6677 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Formolene® L62009B | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Dynaprene® SE9060A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| LNP™ STAT-KON™ QD000I compound | SABIC Innovative Plastics | Nylon 610 | LNP™ STAT-KON™ |