LUBEMID A26 GF25 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2PaCNB_LUBEMID-A26-GF25-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA66 natural first choice. With glass fibres 25%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 to 1.33 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 to 7500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 120 to 130 | MPa | |
| Break | 120 to 130 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 2.0 to 3.0 | % | |
| Break | 2.0 to 3.0 | % | |
| Flexural Modulus 1 | 6500 to 7000 | MPa | ISO 178 |
| Flexural Stress 2 | 160 to 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 to 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 to 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 70 to 80 | J/m | ASTM D256A |
| 23°C 3 | 50 to 60 | kJ/m² | ASTM D256 |
| 23°C | 6.0 to 7.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 7.0 to 8.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 40 to 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 245 to 255 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 245 to 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 235 to 245 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 245 to 255 | °C | ISO 306/A120 |
| -- | 235 to 245 | °C | ISO 306/B120 |
| Melting Temperature | 250 to 265 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech B9706 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| BorPure™ MB6562 | Borealis AG | HDPE | BorPure™ |
| ASTALAC™ ABS M7 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Electrafil® ABS CF25 BK | Techmer Engineered Solutions | ABS | Electrafil® |
| Hostaform® UV90Z XAP2 ™ | Celanese Corporation | PPS | Hostaform® |