HAIPLEN EP50 T7
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2OEGzP_HAIPLEN-EP50-T7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer talcum filled 35%. Available: all colors, UV stabilized (L), heat stabilized (H), anti-static (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.85 | % | |
| Across Flow | 0.85 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 15 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C | 35 | J/m | ASTM D256, ISO 180 |
| 0°C | 45 | J/m | ISO 180, ASTM D256 |
| 23°C | 65 | J/m | ASTM D256, ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ASTM D1525, ISO 306/A 2 1 |
| -- | 75.0 | °C | ASTM D1525, ISO 306/B 3 2 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF30-60 XE-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| TRIBOCOMP® PA66 GF30 TS7 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| Unichem 6811-02 BUSCH | Colorite Polymers | PVC, Unspecified | Unichem |
| Nylene® 2408 HSSP BK | Custom Resins Group | Nylon 6 | Nylene® |
| Kepital® F25-03 LOF | KEP Americas | Acetal (POM) Copolymer | Kepital® |