Delene 3590
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Shanghai Lin Gen Rubber Materials Co., Ltd. |
| Trademark: | Delene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2No0Oi_Delene3590.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Delene 3590 is a thermoplastic elastomer (TPE) material,. This product is available in the Asia-Pacific region and is processed by extrusion or injection molding. The main features of Delene 3590 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 10.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 220 | % | ASTM D412 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.0 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 250 | °C | |
| Injection Pressure | 40.0 - 60.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPORAN 0024 V0 13 | Vamp Tech | PPE+PS | VAMPORAN |
| Nypol® PA A2 G30 NTLA011 NR245 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Durethan® BKV 30 XTS1 901510 | LANXESS GmbH | Nylon 6 | Durethan® |
| LNP™ THERMOCOMP™ EX06430H compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| MAJORIS DG304X | AD majoris | PP, Unspecified | MAJORIS |